Titanium Alloy Grade 2 is “unalloyed” titanium offering an excellent balance
of strength and ductility. The material has good toughness and is readily
weldable. This material is very corrosion resistant in highly oxidizing and
mildly reducing environments.
Standard: ASMESB338; ASTM B861; ASTM B862;AMS4942;AMS4945;AMS4944;AMS4943; GB/T3625;
Standard |
Werkstoff No. |
UNS |
Commercial Pure Titanium Grade2 |
3.7035 |
R50400 |
Technical Data Sheet
Chemical Composition |
||||||
Weight % |
Ti |
C |
Fe |
N |
O |
H |
Commercial Pure Titanium Grade2 |
Balance |
0.08 |
0.3 |
0.03 |
0.25 |
0.015 |
Typical Mechanical Properties (Tensile Requirements)
Material |
Tensile Strength, min |
Yield Strength (0.2% Offset) min or range |
Elongation in 4D,min% |
Reduction of Area Min % |
||
ksi |
MPa |
ksi |
MPa |
|||
Commercial Pure Titanium Grade2 |
50 |
345 |
40 |
275 |
20 |
30 |
Titanium Alloy Grade 12 is lightly alloyed near-alpha alloy offering improved strength at elevated temperatures and optimum ASME Code design allowables. The material is readily weldable, and
Titanium Alloy Grade9 Ti-3Al-2.5V alloy is an alpha alloy that is strengthened by cold working. The material exhibits good ductility and toughness. It is used in a wide range of tubular prod
Titanium Alloy Grade 7 with 0.1% palladium is similar to Grade 2, but with improved resistance to general and localized crevice corrosion in a wide range of reducing acid environments, inclu
Ti-6Al-4V ELI Alloy is the most widely used titanium alloy of the alpha-plus beta class, and is also the most common of all titanium alloys. This modification incorporates extra low int